High-Strength Carbon Fiber Board
High-strength industrial insulation board, UL94 V-0 flame retardant, excellent electrical insulation. Thickness 0.3-3.0mm, custom cutting available.
Carbon Fiber fiberglass board is made from electronic-grade fiberglass cloth and flame-retardant epoxy resin.
| 项目 | 规格 |
|---|---|
| Material | Carbon Fiber Carbon Fiber Composite |
| Flame Rating | UL94 V-0 |
| Thickness | 0.3mm - 3.0mm |
| Standard Size | 1220 x 1020mm |
| Temp Resistance | ≥130C |
| Breakdown Voltage | ≥20kV/mm |
| Color | Natural (Yellow-Green) |
| Custom | Any size cutting available |
Contact us for product details and quotes. We respond within 24 hours.
| Thickness (mm) | Standard Sheet (mm) | Weave Pattern | Layers (approx) |
|---|---|---|---|
| 0.3 | 200 x 300 / 300 x 400 | 2/2 Twill / Plain | 3-4 |
| 0.5 | 200 x 300 / 300 x 400 / 400 x 500 | 2/2 Twill / Plain | 5-6 |
| 0.8 | 200 x 300 / 300 x 400 / 400 x 500 | 2/2 Twill / Plain | 8-10 |
| 1.0 | 200 x 300 / 300 x 400 / 400 x 500 | 2/2 Twill / Plain | 10-12 |
| 1.5 | 200 x 300 / 300 x 400 / 400 x 500 | 2/2 Twill | 15-18 |
| 2.0 | 200 x 300 / 300 x 400 / 400 x 500 | 2/2 Twill | 20-24 |
| 3.0 | 200 x 300 / 300 x 400 | 2/2 Twill | 30-36 |
| 4.0 | 200 x 300 / 300 x 400 | 2/2 Twill | 40-48 |
| 5.0 | 200 x 300 / 300 x 400 | 2/2 Twill | 50-60 |
| Property | Value | Notes |
|---|---|---|
| Tensile Strength | =3600 MPa | Carbon fiber reinforced |
| Tensile Modulus | =230 GPa | High stiffness |
| Density | 1.5-1.6 g/cm3 | Much lighter than steel |
| Flexural Strength | =700 MPa | Interlaminar shear |
| Layer Thickness (per ply) | 0.1-0.15mm | Typical 3K tow |
| Surface Finish | 3K 2x2 Twill Weave | Glossy / Matte |
| Max Temperature | 150-200 C | Without degradation |
| Thermal Expansion | Near zero (0.5 x 10^-6/C) | Dimensional stability |
| Property | Carbon Fiber | Aluminum 6061 | Steel 1018 |
|---|---|---|---|
| Density (g/cm3) | 1.5-1.6 | 2.70 | 7.87 |
| Tensile Strength (MPa) | =3600 | =310 | =440 |
| Stiffness (GPa) | =230 | 69 | 207 |
| Strength-to-Weight | Highest | Medium | Low |
| Corrosion Resistance | Excellent | Good | Poor (rusts) |
| CNC Machinability | Good (use carbide) | Excellent | Excellent |
| Cost | High | Medium | Low |
| Industry | Application | Why Carbon Fiber |
|---|---|---|
| UAV / Drone | Frame plates, arms, landing gear | Ultra-light, high stiffness |
| Robotics | Robot arms, end effectors | Lightweight, low inertia |
| Aerospace | Structural panels, brackets | High strength-to-weight |
| Automotive | Interior panels, motor mounts | Lightweight, aesthetics |
| Medical | CT scanner beds, prosthetics | Radio-transparent, light |
| Sports | Drone racing frames, camera rigs | Lightweight, durable |